POLIGRAT E 269
Electropolishing Process for Stainless Steel
You need help? Of course!
You have further questions concerning our chemicals and how to use them?
Please do not hesitate to contact us. You can contact the responsible person of the division Poligrat Chemistry by the following telephone number:
+49 (89) 42778- 450
POLIGRAT E 269 is a high efficient industrial electropolishing process for ferritic, martensitic and austenitic stainless steel, but also for duplex and hasteloy . It achieves bright and smooth surfaces and is widely used for deburring.
The operation range is expanded significantly:
- polishing parameter: 3 – 50 A/dm²
- process temperature: 30 – 90 °C
- consistent results and steady polishing parameters from the beginning up an high metal concentration of approx. 120 g Fe/l
The enormous polishing effect of POLIGRAT E268 gains a high degree of gloss in shorter process time and reduced metal removal. The economical saving can be up to 30% in practice.
Especially ferritic steel gets an improved gloss form-ing even at low process temperature (> 50°C)
The deep polishing effect is improved and good polishing results are obtained at low current density. POLIGRAT E 269 is suited best tor treating thin and large scaled work parts, due to its very low starting current density required to establish a stable polish-ing process.
In consequence of the low metal removal to achieve the optimal degree of gloss is the electrolyte con-sumption reduced up to 30%. The waste costs are reduced accordingly.
The reduction of the current density offer the possi-bility treating larger work pieces more economically. Alternatively the production capacity of automatic systems is increased significantly by a more efficient loading of the parts onto the jigs.
POLIGRAT E 269 is operated as immersion process in suitable tanks. The work pieces can be treated either on jigs or as bulk goods in electropolishing barrels or by a special POLIBOX equipment. Due to the low current density contact or burning marks are avoided to the most possible extend.
POLIGRAT E 269 is suitable for the tampon polish-ing technique too.
POLIGRAT E 269 and the rinse water from the process are acidic and contain the dissolved metal. They have to be treated and disposed according to the statutory laws and regulations.
- high economics
- rapid gloss forming
- current saving (polishing starts at 3 A/dm²)
- deep polishing effect
- low process temperature for ferric and austenitic steel
- suitable for duplex steel
SUPPLY
Single-use canister 50 kg (28 l)
Liquid – ready to use
Barrel 342 kg (200 l)
Liquid – ready to use
IBC 1.710 kg (1.000 l)
Liquid – ready to use
Single-use canister 50 kg (49 l)
Concentrate POLIGRAT E 269 K (1:10)
Mixing for 100 l ready to use electrolyte:
phosphoric acid 85% 50 l
sulfuric acid 96% 40 l
POLIGRAT E 269 K 10 l
Barrel 316 kg (200 l)
Concentrate POLIGRAT E 269 K (1:10)
Mixing for 100 l ready to use electrolyte:
phosphoric acid 85% 50 l
sulfuric acid 96% 40 l
POLIGRAT E 269 K 10 l
IBC 1.580 kg (1.000 l)
Concentrate POLIGRAT E 269 K (1:10)
Mixing for 100 l ready to use electrolyte:
phosphoric acid 85% 50 l
sulfuric acid 96% 40 l
POLIGRAT E 269 K 10 l